Products Description
About rubber seal activated carbon filter
Rubber seal activated carbon filter assembly is designed to provide a reliable and efficient solution for the sealing of various parts of the water purifier system. High-quality materials and precision manufacturing ensure a tight and secure seal, preventing any leaks or contamination.
Function: waterproof seal. These components are engineered to withstand the harsh conditions of water purification, including exposure to chemicals, heat, and pressure.
Advantage of rubber seal activated carbon filter
- High-quality material: Resistant to chemicals, UV radiation, and extreme temperatures.
- Excellent sealing performance.
- Versatility.
- Easy installation.
- Cost-effective solution.
Certification
Application
Our rubber seal components are widely used in various water purifier systems, including:
1. Household water purifier
2. Commercial water purifier
3. Industrial water purification system
Conclusion
Our water purifier rubber seal assemblies provide a reliable and efficient solution for sealing the various components of the water purifier system. A tight and secure seal can be ensured, preventing any leakage or contamination.
Hot Tags: rubber seal activated carbon, China rubber seal activated carbon manufacturers, suppliers, factory, FFKM Rubber O Rings For Semiconductor, Automobile ACM Rubber Seals, Cable Rubber Seals, SBR Seals, Electronic ACM Rubber Seals, Automobile XNBR Rubber Seals
Technical data
| Physical properties | ||||
| Property | Test standard | Value | Unit | |
| Hardness | ISO 48 | 72 | IRHD | |
| Elongation at break | ISO 37 | 210 | % | |
| Tensile strength | ISO 37 | 12.2 | Mpa | |
| Compression set-24 hours at 150 ℃ Slab | ISO 815 | 15 | % | |
| Ageing properties | ||||
| Property | Test standard | Value | Unit | |
| Heating ageing-72 hours at 100 ℃ | ISO188 | |||
| Hardness change | 4 | IRHD | ||
| Elongation at break change | -17.9 | % | ||
| Tensile strength change | -18 | % | ||
| Aging water-166hours at 100 ℃ | ISO 1817 | |||
| Hardness change | -1.2 | Shore A | ||
| Elongation at break change | -1 | % | ||
| Tensile strength change | -8.6 | % | ||
| Volume change | 2.17 | % | ||